This product Group designed for specific application purposes, the construction industry (garden furniture, flor grating, dowel production, pool coating), the automotive industry (non-melt stropor resin and putty polyester) is widely consumed. ETPS (low styrene emission) type resins situated within this group developed with the consideration of environment and human health.
| LAK-1030 | Air drying glossy polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Highly reactive | Finish coat on the flat surfaces of furniture such as tables, cabinet, door, etc. |
Chemical base | Specific | Tensile strength (MPa) | 50 – 60 |
| Forms dry and glossy surface | Gap filling on the upper surface of the metal articles such as buttons, belt buckle, ets |
Application | Spray-up | Tensile elongation (%) | 3 – 4 |
| Has flexible structure and paraffin free | Glossy lacquer on the surface of composite structure with fiber glass or carbon fiber |
Viscosity (cps) | 200 – 300 | Tensile E-modulus (MPa) | 3000 – 4000 |
| Easy to sand after hardening | Manhole covers, loopholes | Thixotropy | No | Flexural strength (MPa) | 90 – 100 |
| Density(g/cm³) | 1,09 – 1,10 | Hardness (GYZJ 935-1) | 70– 72 | ||
| Monomer content (%) | 35 – 37 | Heat distortion temperature (°C) | 56– 59 | ||
| Acid value (mgKOH/g) | 21 – 28 | Water absorption (mg) | 47– 49 | ||
| Gel time (min) | 15 – 25 (*) | ||||
| Exothermic peak (°C) | 180 – 200 (*) | ||||
| Curing system (*) | 1% Co(1%) + 2% MEK P | (**)Test applied after post cure application | |||
| LAK-1030 T | Air drying thixotropic glossy polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | |||
|---|---|---|---|---|---|---|
| Highly reactive | Glossy lacquer on the surface of composite structure with fiber glass or carbon fiber such as wooden dash board, gear shift, etc. |
Chemical base | Orthophthalic | Tensile strength (MPa) | 50 – 60 | |
| Forms dry and glossy surface | Finish coat on the flat surfaces of furniture such as tables, cabinet, door, etc. | Application | Casting | Tensile elongation (%) | 1 – 2 | |
| Has flexible structure and paraffin free | Gap filling on the upper surface of the metal articles such as buttons, belt buckle, etc | Viscosity (cps) | 700 – 900 | Tensile E-modulus (MPa) | 3000 – 4000 | |
| Easy to sand after hardening | Thixotropy | No | Flexural strength (MPa) | 90 – 100 | ||
| Density(g/cm³) | 1,11 – 1,13 | Hardness (GYZJ 935-1) | 70 – 72 | |||
| Monomer content (%) | 33 – 35 | Heat distortion temperature (°C) | 56 – 59 | |||
| Acid value (mgKOH/g) | 18 – 30 | Water absorption (mg) | 47– 49 | |||
| Gel time (min) | 8 – 12 (*) | |||||
| Exothermic peak (°C) | 170 – 180 (*) | |||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**) Test applied after post cure application | ||||
| RP-92 | ORTHO plasticizing type polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | |
|---|---|---|---|
| RP-92 is not a polyester type to be used by itself | Flexibility modification of casting and GRP type polyester resins | Chemical base | Orthophthalic |
| Gives flexibility to polyester resin or gelcoat | Application | Adding to polyester resin | |
| Due to its high softening characteristic, it can be mixed with casting or CTP production type polyesters for preventing breaking and cracking |
Viscosity (cps) | 750 – 900 | |
| Recommended amount of RP-92 in polyester resin is between 3%-15% |
Thixotropy | No | |
| Using with button type resin gives impact resistance to the button | Density(gr/cm3) 20°C | 1,15 – 1,16 | |
| Monomer content (%) | 21 – 23 | ||
| Acid value (mgKOH/g) | 18 – 35 | ||
| Gel time (min) | 15 – 125(*) | ||
| Exothermic peak (°C) | 70 – 90 (*) | ||
| Curing system (*) | 0.6% Co(1%) + 2% MEK P | ||