Chemicals Resistant

This group of gelcoats containing bisphenol and viniyl ester are having top level chemical and temperature resistancy characteristics. Especially preffered fort he production of chemical storage tanks, corrosion resistant surface coatings, boat and other sea vessels.

GIN-913 S ISO/NPG acrylic modified gelcoat- spray up
GIN-913 B ISO/NPG acrylic modified gelcoat- brush
GIN-915 S ISO/NPG acrylic modified marine gelcoat- spray up
GIN-915 B ISO/NPG acrylic modified marine gelcoat- brush
GVE-5 Epoxy vinylester gelcoat- spray up
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Maximum chemical resistance Corrosion resistant surface coatings Chemical base Vinylester Tensile strength (MPa) 70 – 80
High corrosion resistance to chemical environments Chemical material storage tank Application Spray-up Tensile elongation (%) 2,5 – 3,5
High temperature resistance Chemical transport tanks, pipes and fittings Viscosity (cps) 2000 – 4000  Tensile E-modulus (MPa) 3000 – 4000 
Ultimate mechanical resistance Boats, yachts and other sea vehicles Thixotropy Yes Flexural strength (MPa) 150 – 160 
  Military and defense industry applications Density(g/cm³)  1,04 – 1,06    Hardness (GYZJ 934-1) 30– 32
  Mold production Monomer content (%) 41 – 43  Heat distortion temperature (°C) 95– 98
  Construction materials  Gel time (min) 15 – 25 (*) Water absorption (mg) 34– 36
    Exothermic peak (°C) 180 – 200 (*)    
    Curing system (*) 2% MEK P,
pre-accelerated
(**)Test applied after post cure application
GVE-305 Epoxy vinylester gelcoat- brush
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Maximum chemical resistance Corrosion resistant surface coatings Chemical base Vinylester Tensile strength (MPa) 70 – 80
High corrosion resistance to chemical environments Chemical material storage tank Application Brush/Roller Tensile elongation (%) 2,5 – 3,5
High temperature resistance Chemical transport tanks, pipes and fittings Viscosity (cps) 8000 – 10000  Tensile E-modulus (MPa) 3000 – 4000 
Ultimate mechanical resistance Boats, yachts and other sea vehicles Thixotropy Yes Flexural strength (MPa) 150 – 160 
  Military and defense industry applications Density(gr/cm³)  1,07 – 1,09      Hardness (barcol) 30– 32
  Mold production Monomer content (%) 40 – 42   Heat distortion temperature (°C) 95– 98
  Construction materials  Gel time (min) 20 – 30 (*) Water absorption (mg) 34– 36
    Exothermic peak (°C) 180 – 200 (*)    
    Curing system (*) 2% MEK P, pre-accelerated (**)Test applied after post cure application
GIN-3013 ISO/NPG acrylic modified gelcoat- brush
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Used as finished gelcoat Equipments for pools and waterparks Chemical base Isophthalic/NPG Tensile strength (MPa) 60 – 70
Maximum UV resistance Boats and other sea vehicles Application Brush
Roller
Tensile elongation (%) 1,5 – 2,5
High glossy surface Car, bus and truck body parts Viscosity (cps) 8000 – 10000    Tensile E-modulus (MPa) 4000 – 4500 
High chemical resistance Sanitary materials such as kitchen top,kitchen
sink, bath tub
Thixotropy Yes Flexural strength (MPa) 110 – 120      
Ultimate resistance to atmospheric medium Military and defense industry applications Density(g/cm³)  1,11 – 1,13   Hardness (GYZJ 934-1) 30 - 40
High resistance to hydrolysis City furniture and surface coverings Monomer content (%) 32 – 36    Heat distortion temperature (°C) 95 – 97
    Gel time (min) 10 – 20 (*) Water absorption (mg) 30 – 35
    Exothermic peak (°C) 180 – 200 (*)    
    Curing system (*) 1% MEK P, pre-accelerated  
        (**) Test applied as polyester after post cure application

Comments
Available in desired colors

GIN-4013 ISO/NPG acrylic modified gelcoat- spray up
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Used as finished gelcoat Equipments for pools and waterparks Chemical base Isophthalic/NPG Tensile strength (MPa) 60 – 70
Maximum UV resistance Boats and other sea vehicles Application Spray-up Tensile elongation (%) 1,5 – 2,5
High glossy surface Car, bus and truck body parts Viscosity (cps) 2000 – 4000    Tensile E-modulus (MPa) 4000 – 4500 
High chemical resistance Sanitary materials such as kitchen top,
kitchensink, bath tub
Thixotropy Yes Flexural strength (MPa) 110 – 120      
Ultimate resistance to atmospheric medium Military and defense industry applications Density(g/cm³)  1,09 – 1,11   Hardness (GYZJ 934-1) 30 - 40
High resistance to hydrolysis City furniture and surface coverings Monomer content (%) 41 – 45    Heat distortion temperature (°C) 95 – 97
    Gel time (min) 10 – 20 (*) Water absorption (mg) 30 – 35
    Exothermic peak (°C) 200 – 220 (*)    
    Curing system (*) 1% MEK P, pre-accelerated  
        (**) Test applied as polyester after post cure application

Comments
Available in desired colors

GIN-313 ISO/NPG acrylic modified gelcoat- brush
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Used as finished gelcoat Equipments for pools and waterparks Chemical base Isophthalic/NPG Tensile strength (MPa) 60 – 70
Excellent resistance to cracking due
to structural flexibility
Boats and other sea vehicles Application Brush/Roller Tensile elongation (%) 2 – 2,5
Maximum UV resistance Car, bus and truck body parts Viscosity (cps) 8000 – 10000 Tensile E-modulus (MPa) 3500 – 3500 
High glossy surface Sanitary materials such as kitchen top,kitchen sink, bath tub Thixotropy Yes Flexural strength (MPa) 110 – 120      
High chemical resistance Military and defense industry applications Density(g/cm³)  1,11 – 1,13   Hardness (GYZJ 934-1) 35 - 40
Ultimate resistance to atmospheric medium City furniture and surface coverings Monomer content (%) 34– 38     Heat distortion temperature (°C) 83 – 85
High resistance to hydrolysis   Gel time (min) 10 – 20 (*) Water absorption (mg) 40 – 45
    Exothermic peak (°C) 165 – 195 (*)    
    Curing system (*) 1% MEK P, pre-accelerated  
        (**) Test applied as polyester after post cure application

Comments
Available in desired colors

GIN-413 ISO/NPG acrylic modified gelcoat- spray up
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Used as finished gelcoat Equipments for pools and waterparks Chemical base Isophthalic/NPG Tensile strength (MPa) 60 – 70
Excellent resistance to cracking due to structural flexibility Boats and other sea vehicles Application Spray-up Tensile elongation (%) 2 – 2,5
Maximum UV resistance Car, bus and truck body parts Viscosity (cps) 2000 – 4000    Tensile E-modulus (MPa) 3000 – 3500 
High glossy surface Sanitary materials such as kitchen top,kitchen sink, bath tub Thixotropy Yes Flexural strength (MPa) 110 – 120      
High chemical resistance Military and defense industry applications Density(gr/cm³)  1,09 – 1,10   Hardness (GYZJ 934-1) 30 - 40
Ultimate resistance to atmospheric medium City furniture and surface coverings Monomer content (%) 39 – 43    Heat distortion temperature (°C) 83 – 87
High resistance to hydrolysis   Gel time (min) 10 – 20 (*) Water absorption (mg) 40 – 42
    Exothermic peak (°C) 200 – 220 (*)    
    Curing system (*) 1% MEK P, pre-accelerated  
        (**) Test applied as polyester after post cure application

Comments
Available in desired colors