This group of gelcoats designed for sections requiring resistancy to chemicals and water are used for producing sanitary materials, artificial marble, water tanks, refrigiration truck body, modular cabin, roof and exterior coating materials, small size sea vessels. Brush and spray types are available. These performance gelcoats provide perfect reults with İlkester color pigment pastes.
| GN-911 P | ORTHO/NPG acrylic modified gelcoat- spray up |
| GN-911 F | ORTHO/NPG acrylic modified brush type gelcoat |
| GN-417 | ORTHO/NPG acrylic modified gelcoat- spray up |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| High glossy surface | Car, bus, truck body parts | Chemical base | Orthophthalic/NPG | Tensile strength (MPa) | 60 – 70 |
| High UV resistance | Boats and other sea vehicles | Application | Spray-up | Tensile elongation (%) | 1,5 – 2,5 |
| High mechanical resistance | Equipment’s for pools and water slides | Viscosity (cps) | 2000 – 4000 | Tensile E-modulus (MPa) | 4000 – 4500 |
| Sanitary materials such as kitchen top,kitchen sink, bath tub |
Thixotropy | Yes | Flexural strength (MPa) | 110 – 120 | |
| Playground and park equipments | Density(g/cm³) | 1,10 – 1,11 | Hardness (GYZJ 934-1) | 30 - 40 | |
| Modular cabinet | Monomer content (%) | 39 – 41 | Heat distortion temperature (°C) | 85 – 87 | |
| Gel time (min) | 10 – 20 (*) | Water absorption (mg) | 35 – 37 | ||
| Exothermic peak (°C) | 190 – 200 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | ||||
| (**) Test applied as polyester after post cure application | |||||
Comments
Available in desired colors
| GN-317 | ORTHO/NPG acrylic modified gelcoat- brush |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| High glossy surface | Car, bus, truck body parts | Chemical base | Orthophthalic/NPG | Tensile strength (MPa) | 60 – 70 |
| High UV resistance | Boats and other sea vehicles | Application | Brush/Roller | Tensile elongation (%) | 1,5 – 2,5 |
| High mechanical resistance | Equipment’s for pools and water slides | Viscosity (cps) | 8000 – 12000 | Tensile E-modulus (MPa) | 4000 – 4500 |
| Sanitary materials such as kitchen top,kitchen sink, bath tub |
Thixotropy | Yes | Flexural strength (MPa) | 110 – 120 | |
| Playground and park equipments | Density(g/cm³) | 1,11 – 1,13 | Hardness (GYZJ 934-1) | 30 - 40 | |
| Modular cabinet | Monomer content (%) | 34 – 36 | Heat distortion temperature (°C) | 85 – 87 | |
| Gel time (min) | 10 – 20 (*) | Water absorption (mg) | 35 – 37 | ||
| Exothermic peak (°C) | 180 – 190 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | ||||
| (**) Test applied as polyester after post cure application | |||||
Comments
Available in desired colors