Kimyasal ve suya karşı dayanım gerektiren bölümler için üretilmiş olan bu ürün grubu jeİlkotlar özellikle saniter malzeme, suni mermer, su deposu, frigorafik kasa, modüler kabin, çatı ve cephe kaplama malzemeleri, küçük deniz taşıtları üretimi gibi alanlarda kullanılmaktadır. Fırça ve püskürtme tipleri bulunan performans jelkotlar, İlkester pigment pastalar ile mükemmel uyum sağlamaktadır.
| GN-317 | ORTHO/NPG acrylic modified brush type gelcoat |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| High glossy surface | Car, bus, truck body parts | Chemical base | Orthophthalic/NPG | Tensile strength (MPa) | 60 – 70 |
| High UV resistance | Boats and other sea vehicles | Application | Brush Roller |
Tensile elongation (%) | 1,5 – 2,5 |
| High mechanical resistance | Equipment’s for pools and water slides | Viscosity (cps) | 8000 – 12000 | Tensile E-modulus (MPa) | 4000 – 4500 |
| Low water absorption | Sanitary materials such as kitchen top,kitchen sink, bath tub |
Thixotropy | Yes | Flexural strength (MPa) | 110 – 120 |
| Ultimate resistance to atmospheric medium | Playground and park equipments | Density(gr/cm3) 20°C | 1,11 – 1,13 | Hardness (barcol) | 30 - 40 |
| High resistance to hydrolysis | Modular cabinet | Monomer content (%) | 34 – 36 | Heat distortion temperature (°C) | 85 – 87 |
| Gel time (min) | 10 – 20 (*) | Water absorption (mg) | 35 – 37 | ||
| Exothermic peak (°C) | 180 – 190 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | ||||
| (**) Test applied as polyester after post cure application | |||||
Comments
Available in desired colors
| GN-417 | ORTHO/NPG acrylic modified spray-up gelcoat |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| High glossy surface | Car, bus, truck body parts | Chemical base | Orthophthalic/NPG | Tensile strength (MPa) | 60 – 70 |
| High UV resistance | Boats and other sea vehicles | Application | Spray-up | Tensile elongation (%) | 1,5 – 2,5 |
| High mechanical resistance | Equipment’s for pools and water slides | Viscosity (cps) | 2000 – 4000 | Tensile E-modulus (MPa) | 4000 – 4500 |
| Low water absorption | Sanitary materials such as kitchen top,kitchen sink, bath tub |
Thixotropy | Yes | Flexural strength (MPa) | 110 – 120 |
| Playground and park equipments | Density(gr/cm3) 20°C | 1,10 – 1,11 | Hardness (barcol) | 30 - 40 | |
| Modular cabinet | Monomer content (%) | 39 – 41 | Heat distortion temperature (°C) | 85 – 87 | |
| Gel time (min) | 10 – 20 (*) | Water absorption (mg) | 35 – 37 | ||
| Exothermic peak (°C) | 190 – 200 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | ||||
| (**) Test applied as polyester after post cure application | |||||
Comments
Available in desired colors
| GN-505 | GN-505 |