Bu ürün grubu jelkotlar bisfenolik ve vinil ester içerikli olup kimyasal ve ısı dayanımı en üst düzeydedir. Özellikle kimyasal madde depolama tankları ve havuzları, korozyona dayanıklı yüzey kaplamaları, tekne ve diğer deniz araçları üretiminde güvenle kullanılmaktadır.
| GIN-4013 | GIN-4013 |
| GIN-3013 | GIN-3013 |
| GIN-313 | GIN-313 |
| GIN-413 | GIN-413 |
| GVE-305 | Epoxy vinylester brush type gelcoat |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Maximum chemical resistance | Corrosion resistant surface coatings | Chemical base | Vinyl ester | Tensile strength (MPa) | 70 – 80 |
| High corrosion resistance to chemical environments | Chemical material storage tank | Application | Spray-up | Tensile elongation (%) | 2,5 – 3,5 |
| High temperature resistance | Chemical transport tanks, pipes and fittings | Viscosity (cps) | 8000 – 10000 | Tensile E-modulus (MPa) | 3000 – 4000 |
| Ultimate mechanical resistance | Boats, yachts and other sea vehicles | Thixotropy | Yes | Flexural strength (MPa) | 150 – 160 |
| Military and defense industry applications | Density(gr/cm3) 20°C | 1,07 – 1,09 | Hardness (barcol) | 30– 32 | |
| Mold production | Monomer content (%) | 40 – 42 | Heat distortion temperature (°C) | 95– 98 | |
| Construction materials | Gel time (min) | 20 – 30 (*) | Water absorption (mg) | 34– 36 | |
| Exothermic peak (°C) | 180 – 200 (*) | ||||
| Curing system (*) | 2% MEK P, pre-accelerated | (**)Test applied after post cure application | |||
| GVE-5 | Epoxy vinylester spray-up gelcoat |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Maximum chemical resistance | Corrosion resistant surface coatings | Chemical base | Vinyl ester | Tensile strength (MPa) | 70 – 80 |
| High corrosion resistance to chemical environments | Chemical material storage tank | Application | Spray-up | Tensile elongation (%) | 2,5 – 3,5 |
| High temperature resistance | Chemical transport tanks, pipes and fittings | Viscosity (cps) | 2000 – 4000 | Tensile E-modulus (MPa) | 3000 – 4000 |
| Ultimate mechanical resistance | Boats, yachts and other sea vehicles | Thixotropy | Yes | Flexural strength (MPa) | 150 – 160 |
| Military and defense industry applications | Density(gr/cm3) 20°C | 1,04 – 1,06 | Hardness (barcol) | 30– 32 | |
| Mold production | Monomer content (%) | 41 – 43 | Heat distortion temperature (°C) | 95– 98 | |
| Construction materials | Gel time (min) | 15 – 25 (*) | Water absorption (mg) | 34– 36 | |
| Exothermic peak (°C) | 180 – 200 (*) | ||||
| Curing system (*) | 2% MEK P, pre-accelerated |
(**)Test applied after post cure application | |||