Owing to its chemical structure, high HDT and mechanical values, this resin group is resistant to high temperature, chemical and corrosive mediums. UV resistancy characteristic can also be provided. Resins in this group have wide range of consumption purposes for producing chemical material storage tanks, pipes, fuel disposal storage tanks, transportation tanks and sea vessels.
| IR-100 | ISO unsaturated polyester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Car, bus and truck body parts | Chemical base | Isophthalic | Tensile strength (MPa) | 60 - 70 |
| Low volumetric shrinkage | Boats and other sea vehicle | Application | Hand lay-up Filament winding |
Tensile elongation (%) | 1 - 2 |
| Resistant to chemical medium | Chemical material storage tanks | Viscosity (cps) | 750 - 900 | Tensile E-modulus (MPa) | 4000-5000 |
| High mechanical strength and HDT |
GRP pipes | Thixotropy | No | Flexural strength (MPa) | 130- 140 |
| Construction materials | Density(g/cm³) | 1,10 - 1,12 | Hardness (GYZJ 934-1) | 40 - 42 | |
| Monomer content (%) | 33 – 45 | Heat distortion temperature (°C) | 76 - 79 | ||
| Acid value (mgKOH/g) | 11 - 20 | Water absorption (mg) | 37 - 39 | ||
| Gel time (min) | 10 - 18 (*) | ||||
| Exothermic peak (°C) | 175 - 185 (*) | ||||
| Curing system (*) | 1% Co(1%)+1% MEK P | (**) Test applied after post cure application | |||
| IR-100 T | ISO thixotropic unsaturated polyester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Pools and water slide equipments | Chemical base | Isophthalic | Tensile strength (MPa) | 60 - 70 |
| Low volumetric shrinkage | Car, bus and truck body parts | Application | Hand lay-up Spray-up Filament winding |
Tensine elongation (%) | 1 - 2 |
| Resistant to chemical medium | Boats and other sea vehicle | Viscosity (cps) | 750 -1100 | Tensile E-modulus (MPa) | 4000-5000 |
| High mechanical strength and HDT |
Chemical material storage tanks | Thixotropy | Yes | Flexural strength (MPa) | 90 - 100 |
| No dripping during vertical application |
GRP pipes | Density(g/cm³) | 1,10 - 1,11 | Hardness (GYZJ 934-1) | 40 - 42 |
| Construction materials | Monomer content (%) | 39 – 41 | Heat distortion temperature (°C) | 78 - 82 | |
| Acid value (mgKOH/g) | 11 - 20 | Water absorption (mg) | 37 - 39 | ||
| Gel time (min) | 10 - 18 (*) | ||||
| Exothermic peak (°C) | 170 - 180(*) | ||||
| Curing system (*) | 1% Co(1%)+1%MEK P | (**) Test applied after post cure application | |||
Comments
Pre-accelerated type can be produced upon request
| IR-110 T | ISO thixotropic unsaturated polyester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| High UV and environmental strength | Pools and water slide equipments | Chemical base | Isophthalic | Tensile strength (MPa) | 55 - 65 |
| High mechanical strength and HDT | Car, bus and truck body parts | Application | Hand lay-up Spray-up |
Tensine elongation (%) | 1 - 2 |
| Resistant to chemical environment | Boats and other sea vehicle | Viscosity (cps) | 500 - 1000 | Tensile E-modulus (MPa) | 4000-5000 |
| Easy and quick fiber wetting | Chemical material storage tanks | Thixotropy | Yes | Flexural strength (MPa) | 95 - 105 |
| No dripping during vertical application |
Pool filters | Density(g/cm³) | 1,07 - 1,09 | Hardness (GYZJ 934-1) | 40 - 42 |
| Construction materials | Monomer content (%) | 43 – 45 | Heat distortion temperature (°C) | 85 - 88 | |
| Acid value (mgKOH/g) | 11 - 20 | Water absorption (mg) | 33 - 35 | ||
| Gel time (min) | 10 - 18 (*) | ||||
| Exothermic peak (°C) | 170 - 180(*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | (**) Test applied after post cure application | |||
| PV-300 | Bisphenol-A epoxy vinylester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Boats, yachts and other sea vehicles | Chemical base | Vinylester | Tensile strength (MPa) | 70 - 80 |
| Low volumetric shrinkage | Wind turbine blades | Application | Hand lay-up Filament winding |
Tensine elongation (%) | 2,5 - 3,5 |
| Resistance to high temperatures and different thermal environment |
Chemical material storage tanks | Viscosity (cps) | 400 - 500 | Tensile E-modulus (MPa) | 3000-4000 |
| High corrosion resistance in a wide variety of acidic and alkaline medium |
Transportation tanks, pipes and fittings | Thixotropy | No | Flexural strength (MPa) | 150 - 160 |
| High mechanical strength and HDT | Construction materials | Density(g/cm°C) | 1,05 - 1,07 | Hardness (GYZJ 934-1) | 30 - 32 |
| High resistance towards osmosis | Special military and defense applications | Monomer content (%) | 42 – 44 | Heat distortion temperature (°C) | 95 - 98 |
| Acid value (mgKOH/g) | Max. 7 | Water absorption (mg) | 34 - 36 | ||
| Gel time (min) | 25 - 35(*) | ||||
| Exothermic peak (°C) | 180 - 200 (*) | ||||
| Curing system (*) | 0.5% Co(6%)+2%MEK P | (**) Test applied after post cure application | |||
| PV-300 T | Bisphenol-A epoxy vinylester thixotropic resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Boats, yachts and other sea vehicles |
Chemical base | Vinylester | Tensile strength (MPa) | 70 - 80 |
| Low volumetric shrinkage | Wind turbine blades | Application | Hand lay-up Spray-up Filament winding |
Tensine elongation (%) | 2,5 - 3,5 |
| Resistance to high temperatures and different thermal environment |
Chemical material storage tanks | Viscosity (cps) | 750 - 1750 | Tensile E-modulus (MPa) | 3000-4000 |
| High corrosion resistance in a wide variety of acidic and alkaline medium |
Transportation tanks, pipes and fittings | Thixotropy | Yes | Flexural strength (MPa) | 150 - 160 |
| High mechanical strength and HDT | Special applications for military and defense industry |
Density (g/cm³) | 1,04 - 1,05 | Hardness (GYZJ 934-1) | 30 - 32 |
| High resistance towards osmosis | Monomer content (%) | 44 – 45 | Heat distortion temperature (°C) | 95 - 98 | |
| No dripping during vertical application | Acid value (mgKOH/g) | Max. 7 | Water absorption (mg) | 34 - 36 | |
| Gel time (min) | 20- 30 (*) | ||||
| Exothermic peak (C) | 190 - 210 (*) | ||||
| Curing system (*) | 0.5% Co(6%)+2%MEK P | (**) Test applied after post cure application | |||
| PV-200 | Bisphenol-A epoxy vinylester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Boats, yachts and other sea vehicles | Chemical base | Vinylester | Tensile strength (MPa) | 70 - 80 |
| Low volumetric shrinkage | Wind turbine blades | Application | Infusion Hand lay-up Filament winding |
Tensine elongation (%) | 2,5 - 3,5 |
| Resistance to high temperatures and different thermal environment |
Chemical material storage tanks | Viscosity (cps) | 150- 200 | Tensile E-modulus (MPa) | 3000-4000 |
| High corrosion resistance in a wide variety of acidic and alkaline medium |
Transportation tanks, pipes and fittings | Thixotropy | No | Flexural strength (MPa) | 150 - 160 |
| High mechanical strength and HDT | Special military and defense applications | Density (g/cm³) | 1,05 - 1,06 | Hardness (GYZJ 934-1) | 30 - 32 |
| High resistance towards osmosis | Construction materials | Monomer content (%) | 41 – 43 | Heat distortion temperature (°C) | 95 - 98 |
| Acid value (mgKOH/g) | Max. 7 | Water absorption (mg) | 34 - 36 | ||
| Gel time (min) | 20 - 30(*) | ||||
| Exothermic peak (°C) | 160 - 170 (*) | ||||
| Curing system (*) | 0.5% Co(6%)+2%MEK P | (**) Test applied after post cure application | |||
| PV-290 PS | Bisphenol-A epoxy vinylester resin for gratings applications |
| IR-105 LMR | ISO unsaturated polyester resin for RTM applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Boats, yachts and other sea vehicles | Chemical base | Isophthalic | Tensile strength (MPa) | 60 – 70 |
| High quality surface on both sides | Car, bus and truck body parts | Application | RTM | Tensile elongation (%) | 2 – 3 |
| High mechanical strength | Pools and water slide equipments equipments | Viscosity (cps) | 160 – 200 | Tensile E-modulus (MPa) | 3500 – 4500 |
| 10%-15% filler capacity | Construction materials | Thixotropy | No | Flexural strength (MPa) | 90 – 100 |
| Low volumetric shrinkage when filled | Density(g/cm³) | 1,07 – 1,09 | Hardness (GYZJ 934-1) | 40 – 42 | |
| Ideal for molding of wide, large and thick composite parts | Monomer content (%) | 42 – 44 | Heat distortion temperature (°C) | 82 – 85 | |
| Acid value(mgKOH/g) | 11 – 20 | Water absorption (mg) | 33 – 35 | ||
| Gel time (min) | 20 – 30 (*) | ||||
| Exothermic peak (°C) | 150 – 160 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | (**) Test applied after post cure application | |||
| IR-106 LMR | ISO unsaturated polyester resin for transparent applications |
| IR-3020 BS | ISO unsaturated polyester resin for gratings applications |
| IR-355 | ISO unsaturated polyester resin for pultrusion applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Highly reactive | Structural profiles | Chemical base | Isophthalic | Tensile strength (MPa) | 60 – 70 |
| High mechanical properties | Handrails, walkways and platforms | Application | Pultrusion | Tensile elongation (%) | 2 – 3 |
| High chemical properties | Traffic and road safety equipments | Viscosity (cps) | 800 – 900 | Tensile E-modulus (MPa) | 3000 – 4000 |
| High heat distortion temperature (HDT) | Thixotropy | No | Flexural strength (MPa) | 130 – 140 | |
| Suitable for mass production | Density(g/cm³) | 1,11 – 1,13 | Hardness (GYZJ 934-1) | 40 – 42 | |
| Monomer content (%) | 34 – 36 | Heat distortion temperature (°C) | 98 – 102 | ||
| Acid value (mgKOH/g) | 18 – 30 | Water absorption (mg) | 28 – 32 | ||
| Gel time (min) | 20 – 25 (*) | ||||
| Exothermic peak (°C) | 190 – 210 (*) | ||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**) Test applied after post cure application | |||