High temperature resistancy and mechanical values possessing resins of this Group have a wide range of application area. Some of them are autormotive, bus and truck body parts, roof and building exterior coatings, natural gas and electric boxes.
| P-1179 | ORTHO SMC type polyester resin |
| INR-545 | ISO/NPG SMC-BMC type polyester resin |
| P-1158 | ORTHO BMC type polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Forms smooth and glossy surface | Small and large automotive parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55 – 65 |
| Low volumetric shrinkage | Electrical and natural gas boxes | Application | BMC | Tensile elongation (%) | 1,5 – 2,5 |
| High mechanical properties | Small machine equipments | Viscosity (cps) | 800 – 1200 | Tensile E-modulus (MPa) | 3500 – 4500 |
| High heat distortion temperature (HDT) | Thixotropy | No | Flexural strength (MPa) | 90 – 105 | |
| Density(g/cm³) | 1,11 – 1,13 | Hardness (GYZJ 934-1) | 42 – 44 | ||
| Monomer content (%) | 35 – 37 | Heat distortion temperature (°C) | 115 – 118 | ||
| Acid value (mgKOH/g) | 18 – 24 | Water absorption (mg) | 35– 37 | ||
| Gel time (min) | 25 – 40 (*) | ||||
| Exothermic peak (°C) | 200 – 220 (*) | ||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**)Test applied after post cure application | |||
| P-1186 PLUS | ORTHO SMC – BMC type polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Forms smooth and glossy surface especially for paint finish parts |
Small and large automotive parts (car, bus, truck and tractor parts) |
Chemical base | Orthophthalic | Tensile strength (MPa) | 45 – 55 |
| Low volumetric shrinkage | Electrical and natural gas boxes | Application | SMC – BMC | Tensile elongation (%) | 1 – 2 |
| Highly reactive | Street lighting products | Viscosity (cps) | 1000 – 3000 | Tensile E-modulus (MPa) | 3000 – 4000 |
| High mechanical properties | Manhole covers, loopholes | Thixotropy | No | Flexural strength (MPa) | 80 – 90 |
| High heat distortion temperature (HDT) | Density(g/cm³) | 1,11 – 1,13 | Hardness (GYZJ 934-1) | 42 – 44 | |
| Monomer content (%) | 33 – 35 | Heat distortion temperature (°C) | 104 – 106 | ||
| Acid value (mgKOH/g) | Max. 26 | Water absorption (mg) | 35 – 37 | ||
| Gel time (min) | 40 – 60 (*) | ||||
| Exothermic peak (°C) | 190 – 200 (*) | ||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**)Test applied after post cure application | |||
| P-1186 | ORTHO SMC – BMC type polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Forms smooth and glossy surface | Small and large automotive parts (car, bus, truck and tractor parts) |
Chemical base | Orthophthalic | Tensile strength (MPa) | 45 – 55 |
| Highly reactive | Electrical and natural gas boxes | Application | SMC – BMC | Tensile elongation (%) | 1 – 2 |
| Low volumetric shrinkage | Street lighting products | Viscosity (cps) | 1000 – 3000 | Tensile E-modulus (MPa) | 3000 – 4000 |
| High mechanical properties | Manhole covers, loopholes | Thixotropy | No | Flexural strength (MPa) | 80 – 90 |
| High heat distortion temperature (HDT) | Density(g/cm³) | 1,11 – 1,12 | Hardness (GYZJ 934-1) | 42 – 44 | |
| Monomer content (%) | 34 – 36 | Heat distortion temperature (°C) | 104 – 106 | ||
| Acid value (mgKOH/g) | Max. 26 | Water absorption (mg) | 35– 37 | ||
| Gel time (min) | 20 – 40 (*) | ||||
| Exothermic peak (°C) | 190 – 200 (*) | ||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**)Test applied after post cure application | |||