Yüksek ısı dayanımı ve mekanik değerlere sahip bu grup reçineler çok geniş bir kullanım alanına sahiptir. Bunlardan bazıları, otomotiv, otobüs ve kamyon parçaları, çatı ve cephe kaplamaları, doğalgaz ve elektrik kutularıdır. Parlak yüzey elde etmek istendiği takdirde İlkalem üretimi olan LAK polyester katkılı ürünler tercih edilmelidir.
| P-1158 | ORTHO BMC type unsaturated polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Forms smooth and glossy surface | Small and large automotive parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55 – 65 |
| Low volumetric shrinkage | Electrical and natural gas boxes | Application | BMC | Tensile elongation (%) | 1,5 – 2,5 |
| High mechanical properties | Small machine equipments | Viscosity (cps) | 800 – 1200 | Tensile E-modulus (MPa) | 3500 – 4500 |
| High heat distortion temperature (HDT) | Thixotropy | No | Flexural strength (MPa) | 95 – 105 | |
| Density(gr/cm3) 20°C | 1,11 – 1,13 | Hardness (barcol) | 42 – 44 | ||
| Monomer content (%) | 35 – 37 | Heat distortion temperature (°C) | 115 – 118 | ||
| Acid value (mgKOH/g) | 18 – 24 | Water absorption (mg) | 35– 37 | ||
| Gel time (min) | 25 – 40 (*) | ||||
| Exothermic peak (°C) | 200 – 220 (*) | ||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**)Test applied after post cure application | |||
| P-1186 | ORTHO SMC – BMC type unsaturated polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Forms smooth and glossy surface especially for paint finish parts |
Small and large automotive parts (car, bus, truck and tractor parts) |
Chemical base | Orthophthalic | Tensile strength (MPa) | 45 – 55 |
| Low volumetric shrinkage | Electrical and natural gas boxes | Application | SMC – BMC | Tensile elongation (%) | 1 – 2 |
| Highly reactive | Street lighting products | Viscosity (cps) | 1000 – 3000 | Tensile E-modulus (MPa) | 3000 – 4000 |
| High mechanical properties | Manhole covers, loopholes | Thixotropy | No | Flexural strength (MPa) | 80 – 90 |
| High heat distortion temperature (HDT) | Density(gr/cm3) 20°C | 1,11 – 1,12 | Hardness (barcol) | 42 – 44 | |
| Monomer content (%) | 34 – 36 | Heat distortion temperature (°C) | 104 – 106 | ||
| Acid value (mgKOH/g) | Max. 26 | Water absorption (mg) | 35– 37 | ||
| Gel time (min) | 20 – 40 (*) | ||||
| Exothermic peak (°C) | 190 – 200 (*) | ||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**)Test applied after post cure application | |||
| P-1186 PLUS | ORTHO SMC – BMC type unsaturated polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Forms smooth and glossy surface especially for paint finish parts |
Small and large automotive parts (car, bus, truck and tractor parts) |
Chemical base | Orthophthalic | Tensile strength (MPa) | 45 – 55 |
| Low volumetric shrinkage | Electrical and natural gas boxes | Application | SMC – BMC | Tensile elongation (%) | 1 – 2 |
| Highly reactive | Street lighting products | Viscosity (cps) | 1000 – 3000 | Tensile E-modulus (MPa) | 3000 – 4000 |
| High mechanical properties | Manhole covers, loopholes | Thixotropy | No | Flexural strength (MPa) | 80 – 90 |
| High heat distortion temperature (HDT) | Density(gr/cm3) 20°C | 1,11 – 1,13 | Hardness (barcol) | 42 – 44 | |
| Monomer content (%) | 33 – 35 | Heat distortion temperature (°C) | 104 – 106 | ||
| Acid value (mgKOH/g) | Max. 26 | Water absorption (mg) | 35– 37 | ||
| Gel time (min) | 40 – 60 (*) | ||||
| Exothermic peak (°C) | 190 – 200 (*) | ||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**)Test applied after post cure application | |||