Özel kullanım alanlarına yönelik dizayn edilmiş bu ürün grubu, yapı sektörü (bahçe mobilyaları), inşaat sektörü (ızgara yer kaplama, dübel üretimi, havuz kaplama), otomotiv sektöründe (stropor eritmeyen polyester ve macun polyesteri) yaygın olarak kullanılmaktadır. Bu grup içerisinde yer alan ETPS (düşük stiren emüsyonlu) tipi reçineler çevre ve insan sağlığı düşünülerek geliştirilmiştir.
| LAK-1030 | Air drying glossy unsaturated polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Highly reactive | Finish coat on the flat surfaces of furniture such as tables, cabinet, door, etc. |
Chemical base | Specific | Tensile strength (MPa) | 50 – 60 |
| Forms dry and glossy surface | Gap filling on the upper surface of the metal articles such as buttons, belt buckle, ets |
Application | Spray-up | Tensile elongation (%) | 3 – 4 |
| Has flexible structure and paraffin free | Glossy lacquer on the surface of composite structure with fiber glass or carbon fiber |
Viscosity (cps) | 200 – 300 | Tensile E-modulus (MPa) | 3000 – 4000 |
| Easy to sand after hardening | Manhole covers, loopholes | Thixotropy | No | Flexural strength (MPa) | 90 – 100 |
| Density(gr/cm3) 20°C | 1,09 – 1,10 | Hardness (barcol) | 70– 72 | ||
| Monomer content (%) | 33 – 37 | Heat distortion temperature (°C) | 56– 59 | ||
| Acid value (mgKOH/g) | 21 – 28 | Water absorption (mg) | 47– 49 | ||
| Gel time (min) | 15 – 25 (*) | ||||
| Exothermic peak (°C) | 180 – 200 (*) | ||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**)Test applied after post cure application | |||
| LAK-1030 T | Air drying thixotropic glossy unsaturated polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | |||
|---|---|---|---|---|---|---|
| Highly reactive | Glossy lacquer on the surface of composite structure with fiber glass or carbon fiber such as wooden dash board, gear shift, etc. |
Chemical base | Orthophthalic | Tensile strength (MPa) | 50 – 60 | |
| Forms dry and glossy surface | Finish coat on the flat surfaces of furniture such as tables, cabinet, door, etc. | Application | Casting | Tensile elongation (%) | 1 – 2 | |
| Has flexible structure and paraffin free | Gap filling on the upper surface of the metal articles such as buttons, belt buckle, etc | Viscosity (cps) | 700 – 900 | Tensile E-modulus (MPa) | 3000 – 4000 | |
| Easy to sand after hardening | Thixotropy | No | Flexural strength (MPa) | 70 – 80 | ||
| Density(gr/cm3) 20°C | 1,11 – 1,13 | Hardness (barcol) | 40 – 42 | |||
| Monomer content (%) | 33 – 35 | Heat distortion temperature (°C) | 76 – 79 | |||
| Acid value (mgKOH/g) | 18 – 30 | Water absorption (mg) | 39 – 41 | |||
| Gel time (min) | 8 – 12 (*) | |||||
| Exothermic peak (°C) | 170 – 180 (*) | |||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**) Test applied after post cure application | ||||