CTP el yatırması, fitil sarma, elyaf püskürtme uygulamalarına yönelik, yüksek yük altında deformasyon sıcaklığı (HDT) değerlerine ve mekanik değerlere sahip doymamış polyester reçinelerdir. Otomobil, otobüs ve kamyon parçaları, deniz taşıtları, su kaydırakları, modüler kabin, inşaat malzemeleri, depo, dekoratif CTP mobilyalar gibi ürünlerin üretiminde güvenle kullanılmaktadır.
| P-192 | ORTHO unsaturated polyester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Cars,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 60-70 |
| Low volumetric shrinkage | Boats and other sea vehicles | Application | Hand lay-up Filament winding Hand lay-up Filament winding |
Tensine elongation (%) | 1-2 |
| Modular cabinet | Thixotropy | No | Tensile E-modulues (MPa) | 4000-500 | |
| Water tank | Viscosity (cps) | 500 - 600 | Flexural strength (MPa) | 170-180 | |
| Decorative FRP furniture | Density g(cm) | 1,12 - 1,14 | Hardness (GYZJ 934-1) | 40-42 | |
| Construction materials | Monomer content (%) | 33 - 35 | Heat distortion temperature (C) | 58-61 | |
| Acid value (mgKOH/g) | 18-25 | Water absorption (mg) | 29-31 | ||
| Gel time (min) | 10-18 (*) | ||||
| Exothermic peak (C) | 160-200 (*) | ||||
| Curing system (*) | 1% Co(1%)+1%MEK P | ||||
| P-192 T | ORTHO thixotropic unsaturated polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Cars,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55 – 65 |
| Low volumetric shrinkage | Boats and other sea vehicles | Application | Hand lay-up Spray-up Filament winding |
Tensine elongation (%) | 1-2 |
| No dripping during vertical application | Modular cabinet | Viscosity (cps) | 500 – 1000 | Tensile E-modulus (MPa) | 4000-500 |
| Water tank | Thixotropy | Yes | Flexural strength (MPa) | 140 – 150 | |
| Decorative FRP furniture | Density(gr/cm3) 20°C | 1,11 – 1,12 | Hardness (barcol) | 40-42 | |
| Construction materials | Monomer content (%) | 38 – 40 | Heat distortion temperature (°C) | 72 – 75 | |
| Acid value (mgKOH/g) | 18-25 | Water absorption (mg) | 36 – 38 | ||
| Gel time (min) | 10-18 (*) | ||||
| Exothermic peak (°C) | 160-200 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | ||||
Comments
Can be produced as unaccelerated upon request
| P-116 | ORTHO unsaturated polyester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Cars,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55-65 |
| Highly reactive | Boats and other sea vehicles | Application | Hand lay-up Filament winding |
Tensine elongation (%) | 1-2 |
| Highly reactive | Modular cabinet | Viscosity (cps) | 350 - 400 | Tensile E-modulues (MPa) | 4000-500 |
| Suitable for mass production | Water tank | Thixotropy | No | Flexural strength (MPa) | 140-150 |
| Decorative FRP furniture | Density(gr/cm3) 20°C | 1,10 – 1,12 | Hardness (GYZJ 934-1) | 40-42 | |
| Construction materials | Monomer content (%) | 38 - 40 | Heat distortion temperature (C) | 72 - 75 | |
| Acid value (mgKOH/g) | 18 - 24 | Water absorption (mg) | 36 - 38 | ||
| Gel time (min) | 10 - 15 (*) | ||||
| Exothermic peak (C) | 165 - 185(*) | ||||
| Curing system (*) | 1% Co(1%)+1%MEK P | ||||
| P-1016 | ORTHO unsaturated polyester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Cars,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55-65 |
| Highly reactive | Boats and other sea vehicles | Application | Hand lay-up Filament winding |
Tensine elongation (%) | 1-2 |
| Highly reactive | Modular cabinet | Viscosity (cps) | 350 - 400 | Tensile E-modulues (MPa) | 4000-500 |
| Suitable for mass production | Water tank | Thixotropy | No | Flexural strength (MPa) | 140-150 |
| Decorative FRP furniture | Density(gr/cm3) 20°C | 1,10 – 1,12 | Hardness (GYZJ 934-1) | 40-42 | |
| Construction materials | Monomer content (%) | 38 - 40 | Heat distortion temperature (C) | 72 - 75 | |
| Acid value (mgKOH/g) | 18 - 24 | Water absorption (mg) | 36 - 38 | ||
| Gel time (min) | 10 - 15 (*) | ||||
| Exothermic peak (C) | 165 - 185(*) | ||||
| Curing system (*) | 1% Co(1%)+1%MEK P | ||||
| P-1017 ETPS | ORTHO thixotropic low styrene emission GRP type resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Cars,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55 - 65 |
| Low volumetric shrinkage | Boats and other sea vehicles | Application | Hand lay-up Cold press Filament winding |
Tensine elongation (%) | 1 - 2 |
| sdfsdf | Modular cabinet | Viscosity (cps) | 500 - 1000 | Tensile E-modulues (MPa) | 4000-5000 |
| sdfsdf | Water tank | Thixotropy | Yes | Flexural strength (MPa) | 85 - 95 |
| Accepts up to 20% fiber filling | Decorative FRP furniture | Density g(cm) | 1,10 – 1,12 | Hardness (GYZJ 934-1) | 40 - 42 |
| Construction materials | Monomer content (%) | 39 - 41 | Heat distortion temperature (C) | 67 - 70 | |
| Acid value (mgKOH/g) | 18 - 30 | Water absorption (mg) | 30 - 32 | ||
| Gel time (min) | 15 - 25 (*) | ||||
| Exothermic peak (C) | 160 - 185 (*) | ||||
| Curing system (*) | 1% Co(1%)+1%MEK P | ||||
| P-920 | P-920 |