Tekstil sektörüne yönelik tasarlanmış bu grup polyester reçineler santrifüj döküm ve çubuk döküm üretimlerinde kullanılmaktadır. Renklendirmek için kullanılan İlkester pigment pastalar ile bu reçinelerin uyumu son derece mükemmeldir.
| P-128D | ORTHO unsaturated polyester resin for centrifugal casting of button |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Excellent compatibility with pearl, opaque and transparent pigment pastes |
Button production in different sizes | Chemical base | Orthophthalic | Tensile strength (MPa) | 65 – 75 |
| Contains special blue color for excellent whiteness | Application | Centrifugal casting | 1,5 – 2,5 | ||
| Viscosity (cps) | 1000 – 1200 | Tensile E-modulus (MPa) | 2500 – 3500 | ||
| Thixotropy | No | Flexural strength (MPa) | 140 – 150 | ||
| Density(gr/cm3) 20°C | 1,12 – 1,14 | Hardness (GYZJ 934-1) | 34 – 36 | ||
| Monomer content (%) | 28 – 30 | Heat distortion temperature (C) | 51 – 54 | ||
| Acid value (mgKOH/g) | 18 – 35 | Water absorption (mg) | 52 – 54 | ||
| Gel time (min) | 7 – 11 (*) | ||||
| Exothermic peak (C) | 155 – 175 (*) | ||||
| Curing system (*) | 0,6% Co(1%) + 1% MEK P | (**) Test applied after post cure application | |||
| P-405D | ORTHO unsaturated polyester resin for centrifugal casting of button |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Excellent compatibility with pearl, opaque and transparent pigment pastes |
Button production in different sizes | Chemical base | Orthophthalic | Tensile strength (MPa) | 65 – 75 |
| Cured buttons have color stability | Application | Centrifugal casting | Tensile elongation (%) | 2 – 3 | |
| Does not contain heavy metal and phthalate | Viscosity (cps) | 700 – 900 | Tensile E-modulus (MPa) | 2500 – 3500 | |
| Buttons produced by P-405D have color stability | Thixotropy | No | Flexural strength (MPa) | 110 – 120 | |
| Density(gr/cm3) 20°C | 1,11 – 1,13 | Hardness (GYZJ 934-1) | 34 – 36 | ||
| Monomer content (%) | 30 – 32 | Heat distortion temperature (C) | 57 – 60 | ||
| Acid value (mgKOH/g) | 18 – 25 | Water absorption (mg) | 57 – 59 | ||
| Gel time (min) | 7 – 11 (*) | ||||
| Exothermic peak (C) | 160 – 180 (*) | ||||
| Curing system (*) | 1% Co(1%) + 1% MEK P | (**) Test applied after post cure application | |||
| P-104D | ORTHO unsaturated polyester resin for centrifugal casting of button |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Excellent compatibility with pearl, opaque and transparent pigment pastes |
Button production in different sizes | Chemical base | Orthophthalic | Tensile strength (MPa) | 60 – 70 |
| Cured buttons have color stability | Wind turbine blades | Application | Centrifugal casting | 2 – 3 | |
| Cured buttons have uniform flawless gloss | Chemical material storage tanks | Viscosity (cps) | 700 - 900 | Tensile E-modulus (MPa) | 3000-4000 |
| High impact resistance | Transportation tanks, pipes and fittings | Thixotropy | No | Flexural strength (MPa) | 100 – 110 |
| High mechanical strength and HDT | Transportation tanks, pipes and fittings | Density(gr/cm3) 20°C | 1,12 – 1,14 | Hardness (GYZJ 934-1) | 34 – 36 |
| Does not contain heavy metal and phthalate | Monomer content (%) | 32 – 34 | Heat distortion temperature (C) | 51 – 54 | |
| Acid value (mgKOH/g) | 18 – 35 | Water absorption (mg) | 34 - 36 | ||
| Gel time (min) | 7 – 11 (*) | ||||
| Exothermic peak (C) | 145 – 165 (*) | ||||
| Curing system (*) | 0,6% Co(1%) + 1% MEK P | (**) Test applied after post cure application | |||
| P-4004D | P-4004D |